industrial repair agent > high temperature anti wear epoxy metal iron repair compound

high temperature anti wear epoxy metal iron repair compound

BD111H high temperature anti wear abrasion epoxy metal iron
repair compound

Performance features of BD111H high temperature wear resistant metal iron repair
epoxy compound:
1.Black,used for the repairing of phosphating,blackening workpiece defect.
2.With good construction manufacture-ability,without shrinkage after curing.
3.The material after curing has higher strength,can do various machining.

Product usage of BD111H abrasion high temperature resistant iron metal epoxy compound
repair agent:
It is the high performance polymeric metal material which compounded by various alloy material and
modified toughening heat resistant resin,used for the repairing of phosphating,blackening workpiece defect.
The color after repairing is nearly the same as the substrates.it has very high strength,and excellent abrasion
resistance,corrosion resistant and aging resistance.Can do various machining together with the substrates.

Performance index:

Color	Physical state	Density (g/cm3)	Compressive strength (Mpa) GB/1041-2008	Shear strength (Mpa) GB/7124-2008	Tensile strength (Mpa) GB6329-2009	Bending strength (Mpa) GB1042-1999
Cast iron	paste	1.60	98	19	32	56

BD111 iron repair agent curing features table(testing condition:temperature:20-25(℃),RH: 55)
Usable time (min)	Curing time	curing time before full load operation	Working temperature (℃)	The highest temperature resistant (℃)	Hardness (Shore D） ASTM-D-2556
20-40	Room temperature: 24h,or room temperature 2h+80 degree 1h	48 hours	-60-160	180	90

How to use:
1.Surface treatment: Do the coarsening treatment on the surface of pending-repair parts and clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=7:1 or volume ratio A:B=4:1,make A and B two components
mix uniformly,then use it up within specified operation time limit.

3.Coating: Make the mixed-up material be coating on the pending-repair areas layer by layer,
the first layer should be compacted,make it infiltrate fully with the substrates.If the following working procedure
needs machining,should keep out appropriate machining allowance

4.Curing: Cure for 8 hours at the temperature of 25～30℃ before doing machining,
cure for 24 hours before putting it into use,if the temperature is low,should heat it up or prolong the curing time
to promote the curing.

Packaging specification:
Two-component,500g/set,8 sets/carton or 16 sets/carton.

Transportation and storage:
Sealed storage in the cool and dry place.The warranty period is 24 months.Avoid placing it upside down,
knocking against and transporting it as a non-dangerous product during transportation.

Special version:
1.This parameter is for laboratory conditions,due to the actual working condition is more complex,suggest the users to do
the pretest according to actual working condition

2.When the environment temperature is below 15℃,the curing time will prolong,should take proper heating measure

3.When the environment temperature is more than 25℃ or the mixing quantity is too large,the curing speed will expedite,
should properly shorten the application time of coating after mixing.

Product packaging photo of BD111H anti abrasion high temperature resistant metal iron epoxy putty repair compound:

------分隔线----------------------------